Name : SLH52 Epoxy coal tar pitch anti-rust paint

FEATURES

PRODUCT NAME SLH52 Epoxy Coal Tar Pitch Anti-rust Paint
BRIEF High Build Two Pack Self-curing Coal Pitch Epoxy Coating
FEATURES 
-Excellent physical properties and chemical resistance
-Excellent water resistance, microbiological corrosion resistance and plant root corrosion resistance
-High solid, long life
-Good cure properties of low temperature and cathodic protection 
RESISTANCE GUIDE
HEAT RESISTANCE        Up to 120℃ dry heat
WEATHERABILITY       Gloss reduction and cracking will occur with long-term exterior exposure.
SOLVENTS           Resists splash and spillage of most aliphatic hydrocarbon solvents and most common alcohols.
ACIDS            Suitable for splash and spillage to mild acids.
ALKALIS           Suitable for splash and spillage to most alkalis.
SALTS          Excellent resistance to neutral and alkali salts.
WATER           Excellent resistance to immersion in water.
ABRASION           Good when fully cured.
USES: Widely used in Ship, oil platform, bridge, marine facilities, pipeline, etc.
TYPICAL PROPERTIES AND APPLICATION DATA
 COLOR                Brown / Black
 DENSITY                1.4g/ cm3
 SOLIDS BY VOLUME           65%
 SOLIDS BY WEIGHT          79%    
 SPREADING RATE            3.7m2/kg  (125um DFT)
 DRYING TIME(23℃)     Touch  8 Hr  Handle  24 Hr  Full cure  7Days
 OVERCOAT INTERVAL(23℃)     Min 8Hr  Max 7 Days
 STORAGE(dry, cool )   at least 12 months (dry, cool and under cover )
 FLASH POINT       25℃
 PACKAGING        Part A: 21kg  Part B: 3kg  per barrel
 MIXING RATIO (m/m)    Part A:Part B = 7:1
 CURE TIME(23℃)     15min
 POT LIFE(23℃)     4 Hr
DIRECTIONS  Before using stir or using dynamic mixer mixing two components completely, Just mix a good raw material and mixing of raw materials before can not be together. The temperature of stir will >15℃, otherwise thinner should be added for needed viscosity after stir. Overmuch thinner will lead sag and slow cure rate, thin film, thinner should be added after mixed. Practical spreading rates may be reduced 5%—25% for wastage of different application conditions.
APPLICATION  

STEEL: Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3. Primer surface must keep dry and clean. The primer surface of damage, wedding and rusting must be prepared to Sa2.5 or St3. Zinc salt on the primer must be removed by abrasive or fresh water blasting.
Don’t apply at air temperature below 5℃ or above 40℃. Don’t apply at relative humidity above 85% or when air temperature is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind. 
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-15% with Epoxy Thinner X-2. Additional coats may be required to attain specified thickness. 
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-15% of Epoxy Thinner X-2 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-5% of Epoxy Thinner X-2 can be added. Pump ratio is 45:1 and fluid tip is 0.48-0.64 mm.
Overcoating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants. Also can be applied in sequence of coat, glass cloth, coat.  
Recommended previous coat: Zinc Rich Epoxy Primer, Epoxy Anti-rust Primer, Epoxy MIO Intercoating.
Previous coat:  Zinc Rich Epoxy Primer, Anti-rust Epoxy Primer, Epoxy micaceous iron oxide intermediate paint.
CLEAN UP: with Epoxy Thinner X-2.
SAFETY: Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.
Notes: The data in the manual is get from standard experiments and may be vary from different conditions in use. Please refer to the latest manual if the data is altered and we would not inform specially.