PRODUCT NAME SLH38 Antistatic Coatings
BRIEF Two Pack Amine Cured Epoxy Antistatic Primer/Topcoat
FEATURES
-Excellent adhesion, paint film is tough
-Good resistance to abrasion and impact
-Excellent static electricity conductibility
-Excellent chemical resistance
RESISTANCE GUIDE
 HEAT RESISTANCE     Up to 140℃ dry heat
 WEATHERABILITY     Normally not exposed
 SOLVENTS       Resists splash and spillage of most varsol and refined petroleum products
 ACIDS        Suitable for splash and spillage to mild acids
 ALKALIS       Suitable for splash and spillage to strong alkalis
 SALTS         Excellent resistance to neutral and alkali salts
 WATER         Excellent resistance to immersion in fresh and salt water
 ABRASION       Good when fully cured.
USES: Widely used in inner wall of the tank, antistatic and corrosion
TYPICAL PROPERTIES AND APPLICATION DATA
  COLOR       Brown Red (Primer), Light white (Topcoat)
 DENSITY       1.4g/cm3          1.4g/cm3
 SOLIDS BY VOLUME  58%             58%
 SOLIDS BY WEIGHT  76%            76%
 SPREADING RATE   4.1 m2/kg          4.1 m2/kg   (100um DFT)
 DRYING TIME(23℃)   Touch  4 Hr   Handle  24 Hr  Full cure 7Days
 SURFACE RESISTANCE  105Ω<R<109&OMEGA;
 OVERCOAT INTERVAL(23℃)     Min 8 Hr  Max 7 Days 
 STORAGE       at least 12 months (dry, cool and under cover )
 FLASH POINT      26℃
 PACKAGING      Part A: 21kg  Part B: 3kg
 MIXING RATIO (m/m)    Part A : Part B=7:1
 CURE TIME(23℃)     10min
 POT LIFE(23℃)      4 Hr
DIRECTIONS Before using stir or using dynamic mixer mixing two components completely, Just mix a good raw material and mixing of raw materials before can not be together. Rate of cure will vary depending on temperature and other factors such as ventilation, film thickness, humidity, thinner. The temperature of stir will >15℃, otherwise thinner should be added for needed viscosity after stir. 
Overmuch thinner will lead sag and slow cure rate, thin film. Practical spreading rates may be reduced 5-80% for wastage of different application conditions.
APPLICATION  

STEEL: Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3. The surface coated by zinc-rich primer should be dry, clean and no dirt, take the second descaling where film damaged or corrosion, and achieve Sa2.5 level or St3 level. Clear the zinc salt with high pressure fresh water or  sand . Weld and the damage parts processing to Sa2.5 level or St3 level.
Don’t apply at temperatures below 5℃ or above 40℃. Don’t apply at relative humidity above 85% or when the surface is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind.
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-15% with Epoxy Thinner X-2. Additional coats may be required to attain specified thickness. 
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-15% of Epoxy Thinner X-2 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-15% of Epoxy Thinner X-2 can be added. Pump ratio is 23:1 or 32:1 and fluid tip is 0.38-0.43 mm.
 Overcoating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants. 
Previous coat: Zinc Rich Epoxy Primer, or coat Primer directly on the prepared substrate
CLEAN UP: with Epoxy Thinner X-2
SAFETY: Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.