PRODUCT NAME   SLFH53 Epoxy Phenol Novolac Paint
BRIEF High solids For high temperature wastewater, water and oil and various oil tanks and pipeline corrosion.
Can be used for pipeline repairing a film
Good temperature curing
Suggested to adopt high non-gas spraying
FEATURES
 -Used as primer, sealer or intercoat
-Excellent adhesion and sealing power on prepared substrate, good adhesion to next coat
 -Good resistance to abrasion and impact
 -Can be exposed to atmosphere and immersed in water
RESISTANCE GUIDE HEAT RESISTANCE Excellent resistance to heat
 WEATHERABILITY Some chalking will occur with exterior exposure.
 SOLVENTS Resists immersion of most petroleum solvents, gasoline, diesel oil and lubricating oil.
 ACIDS Suitable for splash and spillage to mild acids.
 ALKALIS Exellent for splash and spillage to most alkalis.
 SALTS Resists immersion of neutral and alkali salts.
 WATER Excellent resistance to immersion in fresh and salt water.
 ABRASION Good when fully cured.
USES:Widely used in Ship, oil platform, bridge, marine facilities, pipeline, etc.
TYPICAL PROPERTIES AND APPLICATION DATA  
COLOUR                             color
DENSITY                             1.4g/ cm3
SOLIDS BY VOLUME              65%
SPREADING RATE               5.8m2/kg    (80um DFT)
DRYING TIME(23℃)            Touch ≤4 Hr    Handle ≤24 Hr    Full cure 7Days
OVERCOAT INTERVAL(23℃)      Min 8 Hr   Max 7 Days  
STORAGE (dry, cool )              At least 12 months
FLASH POINT                     28℃
PACKAGING                     Part A: 21kg per barrel   
Part B: 3kg per barrel  
MIXING RATIO (m/m)             Part A : Part B=7:1
CURE TIME(23℃)                 10min  
POT LIFE(23℃)                   4Hr
DIRECTIONS Stir contents of each can thoroughly with a broad flat stirrer using a stirring, lifting action or use a power mixer. Rate of cure will vary depending on temperature and other factors such as ventilation, film thickness, humidity, thinner. The temperature of stir will >15℃, otherwise thinner should be added for needed viscosity after stir. Overmuch thinner will lead sag and slow cure rate, thin film. Practical spreading rates may be reduced 5—25% for wastage of different application conditions.
APPLICATION  STEEL: Round off all rough welds, sharp edges and remove weld spatter. Remove grease, oil and other contaminants. Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3.
Don’t apply at air temperature below 5℃ or above 45℃. Don’t apply at relative humidity above 85% or when air temperature is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind.
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-15% with Epoxy Thinner X-2. Additional coats may be required to attain specified thickness. 
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-15% of Epoxy Thinner X-2 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-15% of Epoxy Thinner X-2 can be added. Pump ratio is 23:1 or 32:1 and fluid tip is 0.38-0.43 mm.
Overcoating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants.
CLEAN UP: with Epoxy Thinner X-2
SAFETY: Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.
Notes: The data in the manual is get from standard experiments and may be vary from different conditions in use. Please refer to the latest manual if the data is altered and we would not inform specially.