PRODUCT NAME SLFH09 Glass flake epoxy phenolic coating
BRIEF Two Pack Glass Flake Enhanced Phenolic epoxy anticorrosive paint
FEATURES  
-Good resistance to abrasion and impact
-Excellent impermeability
-Excellent resistance to acids, alkalis, salts and polluted water in oilfield
-Good adhesion, low shrinkage property during curing
RESISTANCE GUIDE
HEAT RESISTANCE     Up to 200℃ dry heat
WEATHERABILITY    Some chalking and yellowing will occur with exterior exposure, however this will not detract from the resistance properties of the coating
SOLVENTS        Resists splash and spillage of most varsol, refined petroleum
ACIDS         Suitable for splash and spillage to mild acids
ALKALIS        Suitable for splash and spillage to strong alkalis
SALTS         Excellent resistance to neutral and alkali salts
WATER         Excellent resistance to immersion in fresh and salt water
ABRASION       Good when fully cured.
USES: Widely used in steel structure of oil tank, sewage tank, pipeline, water pipe cabin and concrete construction.
TYPICAL PROPERTIES AND APPLICATION DATA
COLOR                   Colors
DENSITY                  1.4g/cm3  
SOLIDS BY VOLUME                65%  
SOLIDS BY WIGHT              80% 
SPREADING RATE               9.29 m2/kg  (80um DFT)
DRYING TIME(23℃)    Touch  4 Hr  Handle  24 Hr  Full cure 7Days
OVERCOAT INTERVAL(23℃)  Min 8 Hr  Max 7 Days  
STORAGE          at least 12 months (dry, cool and under cover )
PACKAGING          Part A: 21kg  Part B: 3kg
MIXING RATIO (m/m)     Part A : Part B=7:1
CURE TIME(23℃)       10min
POT LIFE(23℃)       4 Hr
DIRECTIONS  Before using stir or using dynamic mixer mixing two components completely, Just mix a good raw material and mixing of raw materials before can not be together. Rate of cure will vary depending on temperature and other factors such as ventilation, film thickness, humidity, thinner. The temperature of stir will >15℃, otherwise thinner should be added for needed viscosity after stir.
Overmuch thinner will lead sag and slow cure rate, thin film, thinner should be added after mixed. Practical spreading rates may be reduced 5%—25% for wastage of different application conditions.
APPLICATION  

STEEL: Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3. Weld and the damage parts processing to Sa2.5 level or St3 level.
Don’t apply at temperatures below 5℃ or above 40℃. Don’t apply at relative humidity above 85% or when the surface is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind.
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-15% with Epoxy Thinner X-2. Additional coats may be required to attain specified thickness.
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-15% of Epoxy Thinner X-2 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-5% of Epoxy Thinner X-2 can be added. Pump ratio is 23:1 or 32:1 and fluid tip is 0.38-0.43 mm.
Overcoating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants.
CLEAN UP: with Epoxy Thinner X-2
SAFETY: Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.